【簡介】
摘要：膠粘涂層法是有效提高鎂合金耐腐蝕性能的表面處理技術之一。以E44環(huán)氧樹脂、低分子量650#聚酰胺、云母氧化鐵等為主要原料，制備了適用于AZ31鎂合金基體的防腐膠粘涂層。研究了填料含量對涂層外觀、施工性和耐蝕性能的影響。結果發(fā)現(xiàn)，當填料質(zhì)量分數(shù)為60％、涂層厚度為180～220μm時，防腐膠粘涂層具有良好的外觀及施工性，附著力為1級，耐鹽霧時間168 h。
關鍵詞：鎂合金；膠粘涂層；云母氧化鐵；防腐
中圖分類號：TGl78；TGl74．461 文獻標志碼：A
文章編號：1004—227X(2009)02—0060—03
Preparation of anticorrosive adhesive coating on the surface of AZ3 1 magnesium alloy／／ZHANG Wei*，LI Tao，LIU Yong-feng
Abstract：Adhesive coating is one of the effective surface treatment methods for improving the corrosion resistance of magnesium alloy．An anticorrosive adhesive coating suitable for the surface of AZ3 1 magnesium alloy was prepared with E-44 epoxy resin(EP)，low—molecular—weight 650#polyamide and micaceous ferric oxide as main materials．The effect of filler content on appearance，operability and corrosion resistance of the coating were studied．The results showed that the anticorrosive adhesive coating has good appearance and operability with adhesion grade l and salt spray time of1 68 h when the filler mass fraction is 60％and the coating thickness is l 80—220 pm．
Keywords：magnesium alloy；adhesive coating；micaceous iron oxide；corrosion protection
First．author’S address：College of Material Science and Engineerin9，Chongqing Institute of Technology，Chongqing400050，China
1 前言
由于鎂合金是最輕的結構金屬材料，比鋁合金輕約36％，比鋅合金輕約73％，比鋼輕約77％[l-2]，且具有比強度高，導熱、導電性良好，機加工和再循環(huán)利用性能良好等許多優(yōu)良的特性，而被廣泛應用于航空航天、汽車制造、電子工業(yè)等領域。但鎂合金的化學活性高，在空氣中能自然形成堿式碳酸鹽膜，而且這層膜的防護性很差；因此，鎂合金作為結構材料使用時，必須采取可靠的表面防護措施[3-5]。近年來國內(nèi)外對鎂合金耐蝕表面處理的研究，主要涉及鎂合金表面的化學轉(zhuǎn)化、陽極氧化、微弧陽極氧化、電鍍／化學鍍以及熱噴涂等處理方法。膠粘涂層法是一種具有制造工藝簡便，易于施工，成本低廉等優(yōu)點的表面處理方法。本文采用膠粘涂層法，以E44環(huán)氧樹脂、650#聚酰胺、云母氧化鐵粉等為原料，在AZ31鎂合金基體表面制備了具有良好附著力和防腐性的膠粘涂層。